Thermal recovery of colour centres induced in cubic yttria-stabilized zirconia by charged particle irradiations
Loading...
Date
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
Description
We have used electron paramagnetic resonance to study the thermal annealing of colour centres induced in cubic yttria-stabilized zirconia by swift electron and heavy ion-irradiations. Single crystals were irradiated with 1 or 2-MeV electrons, and 200-MeV 127I, or 200-MeV 197Au ions. Electron and ion beams produce the same colour centres: namely i) an F+-like centre, ii) the so-called T-centre (Zr3+ in a trigonal oxygen local environment), and iii) a hole center. Isochronal annealing was performed up to 973 K. Isothermal annealing was performed at various temperatures on samples irradiated with 2-MeV electrons. The stability of paramagnetic centres increases with fluence and with a TCR treatment at 1373 K under vacuum prior to the irradiations. Two distinct recovery processes are observed depending on fluence and/or thermal treatment. The single-stage type I process occurs for F+-like centres at low fluences in as-received samples, and is probably linked to electron-hole recombination. T-centres are also annealed according to a single-stage process regardless of fluence. The annealing curves allow one to obtain activation energies for recovery. The two-stage type II process is observed only for the F+-like centres in as-received samples, at higher fluences, or in reduced samples. These centres are first annealed in a first stage below 550 K, like in type I, then transform into new paramagnetic centres in a second stage above 550 K. A simple kinetics model is proposed for this process. Complete colour centre bleaching is achieved at about 1000 K.