Optical determination of the superconducting energy gap in electron-doped Pr_{1.85}Ce_{0.15}CuO_4

Simple item page
dc.creatorHomes, C. C.
dc.creatorLobo, R. P. S. M.
dc.creatorFournier, P.
dc.creatorZimmers, A.
dc.creatorGreene, R. L.
dc.date2006-07-14
dc.date2006-11-30
dc.date.accessioned2026-07-07T07:37:10Z
dc.date.available2026-07-07T07:37:10Z
dc.descriptionThe optical properties of single crystal Pr_{1.85}Ce_{0.15}CuO_4 have been measured over a wide frequency range above and below the critical temperature (T_c \simeq 20 K). In the normal state the coherent part of the conductivity is described by the Drude model, from which the scattering rate just above T_c is determined to be 1/τ\simeq 80 cm^{-1}. The condition that \hbar/τ\approx 2k_B T near T_c appears to be a general result in many of the cuprate superconductors. Below T_c the formation of a superconducting energy gap is clearly visible in the reflectance, from which the gap maximum is estimated to be Δ_0 \simeq 35 cm^{-1} (4.3 meV). The ability to observe the superconducting energy gap in the optical properties favors the nonmonotonic over the monotonic description of the d-wave gap. The penetration depth for T\ll T_c is λ\simeq 2000 Å, which when taken with the estimated value for the dc conductivity just above T_c of σ_{dc} \simeq 35 \times 10^3 Ω^{-1}cm^{-1} places this material on the general scaling line for the cuprates defined by 1/λ^2 \propto σ_{dc}(T\simeq T_c) \times T_c. This result is consistent with the observation that 1/τ\approx 2Δ_0, which implies that the material is not in the clean limit.
dc.descriptionDiscussion has been expanded and reorganized; 9 pages, 6 figures
dc.identifierhttps://arxiv.org/abs/cond-mat/0607377
dc.identifierhttp://arxiv.org/abs/cond-mat/0607377
dc.identifierPhys. Rev. B 74, 214515 (2006)
dc.identifierdoi:10.1103/PhysRevB.74.214515
dc.identifier.urihttp://salesiana.dossiersoluciones.com/handle/123456789/120682
dc.subjectSuperconductivity
dc.titleOptical determination of the superconducting energy gap in electron-doped Pr_{1.85}Ce_{0.15}CuO_4
dc.typetext